Carbamate and carbonate salts of tertiary amines

ABSTRACT

Novel carbamic and carbonic acid derivatives are provided by simultaneous reaction of a secondary amine and a tertiary amine with carbon dioxide. These derivatives correspond in general to the formula ##STR1## in which R 1  and R 2  may be individual substituents attached to the N or together form with N a heterocyclic moiety; R 3 , R 4 , R 5  may be individual short chain alkyl or hydroxyalkyl substituents on the N or form therewith a monocyclic or bicyclic heterocyclic moiety. These described compounds find particular use as heat activatable delayed action catalysts especially for use in polyurethane formulations.

This is a division of application Ser. No. 354,844, filed Mar. 4, 1982, now U.S. Pat. No. 4,467,089.

BACKGROUND OF THE INVENTION

The present invention relates to the compositon and synthesis of novel carbonic and carbamic acid derivatives, particularly tertiary amine salts of substituted carbamic and carbonic acids, and to their use particularly as delayed action urethane catalysts.

Carbamic acid, also sometimes designated as aminoformic acid, is not known in the free state. Salts of carbonic acid as well as certain esters thereof are known, including among these metal salts, the ammonium salt, and alkyl esters (urethanes).

Ammonium carbamate has been prepared by reaction of dry ice and liquid ammonia. The preparation of certain alkyl ammonium carbamates, stated to be useful as softening and anti-static agents for fabrics are disclosed in U.S. Pat. No. 3,962,100. The therein disclosed carbamate compounds are prepared by dissolving a primary or secondary long chain alkyl amine in an alcohol solvent and bubbling carbon dioxide through the solution or by reaction of the amine with solid CO₂. The obtained compounds correspond to the general formula: ##STR2## wherein R₁ is hydrogen or alkyl, R₂ is a long chain alkyl group, R₃ and R₄ each is hydrogen or alkyl.

The use of tertiary amine compounds as catalysts and/or co-catalysts in the promotion of isocyanate reactions such as in the preparation of polyurethanes, is well known and certain of these are extensively employed in industry; as for example triethylenediamine, also known as diazabicyclo(2.2.2)octane. Triethylenediamine and other tertiary amine catalysts have also been used or proposed for use in the form of their salts combined with carboxylic acids, so as to stabilize the amine in certain stored compositions or to delay the catalytic effect of the amine in use. See for example, U.S. Pat. No. 3,767,602, which discloses the use of formates and acetates of certain tertiary amine catalysts; including, in addition to such salts of triethylenediamine and methyltriethylenediamine, those of dimethylaminoethyl morpholine, bis-(dimethylaminoethyl)ether, hydroxypropylimidazole, tetramethylbutylenediamine.

Mixtures of the diformate salt of triethylenediamine and hydroxypropyl imidazole in combination with tin catalysts such as tin octoate are known to be useful as delayed action catalysts (DAC), i.e. those which initially delay and then catalyze the polyurethane reactions; see U.S. Pat. No. 3,728,291. Such DAC catalysts extend the cream time to permit the polyurethane reaction to penetrate the intricate parts of the mold and to extend the gelation time as the resulting foam on gelling becomes intractable and resists molding, but to rapidly catalyze the subsequent polymerization rate so that the rise and cure times are comparable to non-DAC catalysts.

SUMMARY OF THE INVENTION

In accordance with the present invention there are provided certain tertiary amine salts of N-substituted carbamic acid and of carbonic acid which, among other possible useful applications, have particular utility as thermally activatable catalysts for polyurethane production and for curing of epoxies. The novel compounds of the invention correspond to the following general structural formula: ##STR3## where R₁ and R₂ can independently be alkyl groups of 1 to 20 carbon atoms, which alkyl groups may contain one or more hydroxyl groups, or R₁ and R₂ together can be a carbon atom containing chain joined to N to form a hetero ring, such as for example imidazole, morpholine, piperazine, and the like. R₃, R₄ and R₅ can independently be alkyl groups of 1 to 3 carbons, hydroxy alkyl groups of up to 3 carbons, or they can be organic radicals joined wherein R₃ and R₄ or R₃ and R₅ can be joined to form a monocyclic or bicyclic hetero ring comprising tertiary nitrogen, such as in triethylene diamine, quinuclidine, N-alkyl piperazine, N-alkyl morpholine, and the like. In addition, one of these R groups can be an ethylene radical attached to another dialkylamino alkyl group by oxygen to form a ditertiary amine of the formula: ##STR4## where each of the R₆ substituents is an alkyl group of up to 3 carbon atoms; n and m are independently 2 or 3.

Compounds of formula I or II are prepared by reacting a non-hindered tertiary amine in aqueous or glycolic solvent with carbon dioxide in the presence or absence of secondary amine according to the following reactions: ##STR5##

The compounds of the invention are characterized either by having at one end a secondary amine moiety and at the other a tertiary amine salt of the carbamic acid, or by a tertiary amine salt of the carbonic acid. Upon being heated to moderate temperatures in the order of about 50°-100° C., they decompose irreversibly with the evolution of carbon dioxide, thus freeing the tertiary amines. Because of this property, the compounds of the invention find utility as thermally activatable catalysts for polyurethane and for epoxy curing. They can also be used as blowing agents in various plastic formulations.

In the preferred reactions, the secondary and tertiary amines are brought together in equimolar proportions in the presence of excess carbon dioxide and under mild pressure of about 1-6 atmospheres. Thus, the secondary amine reacts with CO₂ to form the corresponding di-substituted carbonic acid, which in turn reacts with the tertiary amine to form the desired salt or alternatively the carbon dioxide reacts with water to form carbonic acid which is trapped by the tertiary amine to yield the amine salt of carbonic acid.

DETAILED DESCRIPTION

Illustrative of the novel carbamate compounds of the invention, although not limited thereto, are the following, prepared by reaction of a secondary and tertiary amine with CO₂ : ##STR6## prepared by reaction of CO₂ with dibutyl amine and ethyldimethyl amine; ##STR7## from diethanolamine and N-methyl morpholine; ##STR8## from dimethyl amine and triethylene diamine (TEDA); ##STR9## from morpholine and dimethyl ethanolamine; ##STR10## from diethanolamine and bis(N,N'-dimethylamino)-ethyl ether.

Illustrative examples of the novel carbonate compounds of this invention, although not limited thereto, are the following in which water, carbon dioxide and a tertiary amine are rected as indicated below: ##STR11##

EXAMPLE 1

Into a round bottomed flask there was charged 400 parts by weight of diethylene glycol solvent, 105 parts of diethanol amine and 112 parts of triethylenediamine (equimolar parts of reactants). The mixture was stirred until complete solution was obtained. A CO₂ generating device (dry ice in an Erlenmeyer flask) was then connected to the stirring reaction mixture and CO₂ allowed to bubble in for one day under pressure of 200 ml of water. At the end of this period the flask containing the reaction mixture was weighed and a weight gain of 36 parts was noted, due to the reacted CO₂.

The product was analyzed by nuclear magnetic resonance (NMR) spectroscopy. The NMR analysis showed the product of Example 1 to contain the carbamic acid salt of triethylenediamine and diethylene glycol. The analysis as shown in Table I was carried out at ˜25° C. using D₂ O as the solvent. ##STR12##

                  TABLE I                                                          ______________________________________                                         NMR Analysis of Product From Example 1                                                H'NMR             C.sup.13 NMR                                          Proton/                                                                               Chemical          Chemical  Integra-                                    Carbon Shift, ppm (Multiplicity)                                                                        Shift, ppm                                                                               tion (area)                                 ______________________________________                                         A      3.25 (triplet overlaps H&I)                                                                      51.2      2.0                                         B      3.65 (triplet overlap H&I)                                                                       61.7      2.5                                         C      2.83 (singlet)    4 5       12.7                                        D      2.85 (triplet overlaps C)                                                                        50.2      2.2                                         E      3.5 (triplet)     58.5      2.0                                         F      --                161       1.0                                         G      --                163.8     2.0                                         H      3.6-6.9 (overlap A&B)                                                                            61        8.6                                         I      3.6-3.9 (overlap A&B)                                                                            72.5      8.6                                         ______________________________________                                    

NMR Analysis shows that the product is a mixture of the carbamate and carbonate salts of triethylenediamine. The ratio of carbamate to carbonate is about 2/1.

EXAMPLES 2-4

Into a round bottomed flask equipped with a stirrer and a gas inlet tube, there was charged water and/or diethylene glycol and equimolar parts of a secondary and a tertiary amine. The flask was tared and CO₂ gas bubbled in. The weight of the reaction mixture was periodically checked for CO₂ absorption. When about an equimolar amount of CO₂ was absorbed, the reaction was stopped and the product analyzed by NMR. Table II below summarizes the analytical results obtained on products of Examples 2, 3, and 4.

    TABLE II       NMR Analysis of Products from Examples 2-4 NMR Analysis Ex-      Chemical H' NMR  C.sup.13 NMR   am-  Secondary Tertiary Structure of the       Shift, Multi- Inte- Chemical Multi- Inte- ple Solvent Amine Used Amine      Used Products Obtained  ppm plicity gration Shift plicity gration                    2 water morpholine TEDA       ##STR13##       ABCDE 3.253.752.993.533.75 triplet(Overlap D)tripletsinglettriplettriple      t 4.13.81.34.03.8 Overlap C65.5945.32Overlap C67.82 ----triplet----      --0.242.54--0.54       ##STR14##        FG ---- ---- ---- 163.99161.85 ---- 0.210.20  3 DEG, water, morpholine      TEDA       ##STR15##       ABC 3.243.652.88 complextripletsinglet ------ 44.366.3845.32 triplettrip      lettriplet 2.76.7735.52       ##STR16##       DE 3.6-3.73.5-3.7 ComplexComplex ---- 72.4461.13 triplettriplet      21.3521.55       ##STR17##        3 DEG water morpholine TEDA   F 3.65 Overlap -- 67.36 triplet 7.69        G 3.5 Overlap D & E -- 45.09 triplet 5.9       H -- -- -- 163.45      singlet 3.22       I -- -- -- 161.13 singlet 0.45 4 DPG morpholine      bis-(dimethyl-    amino ethyl)ether       ##STR18##       ABCDEFGHIJ 3.523.72.63.053.65----3.253.651.1 triplet(Overlap E)singlettr      ipletoverlaped----triplet tripletdoublet -------------------- 4 56      543.557.067.0163.2160.3456519 -------------------- --------------------       ##STR19##       ##STR20##       ##STR21##       ##STR22##

It is evident from carbon 13 NMR shown in Table 2 above that both the carbamate and the carbonate salts of tertiary amines were formed. The amount of carbamate was greater than the carbonates by a ratio of at least 2:1.

EXAMPLES 5-7

Into a round bottomed flask equipped as in Example 1 was charged 1 mole of tertiary amine and 100-500 cc of water. The flask was connected to a carbon dioxide cylinder by means of gas inlet adaptor and rubber tubing and to a burette containing 500 cc of Nujol oil by means of gas outlet and rubber tubing. The burette of Nujol oil was used to maintain a pressure greater than atmospheric on the reaction vessel. CO₂ was bubbled in with stirring until a gain of 1 mole of CO₂ was realized. The reaction mixture was then stopped and the flask was allowed to stand at atmospheric pressure and at ambient temperature overnight. The mixture was then analyzed by NMR. The tertiary amine carbonate salts made by this method and their analysis are shown on Table III below.

                                      TABLE III                                    __________________________________________________________________________     NMR Analysis of Products from Examples 5-7                                                                      NMR Analysis                                  Ex-                                Chemical                                                                            H' NMR   C.sup.13 NMR                  am-     Tertiary Structure of the  Shift,                                                                              Multi-                                                                              Inte-                                                                              Chemical                                                                             Multi-                                                                             Inte-               ple                                                                               Solvent                                                                             Amine Used                                                                              Products Obtained ppm  plicity                                                                             gration                                                                            Shift plicity                                                                            gration             __________________________________________________________________________     5  water                                                                               dimethyl- ethanol- amine                                                                 ##STR23##      A B C D                                                                          2.74 3.10 3.76 --                                                                   singlet triplet triplet --                                                          13.2 4.5 4.3 --                                                                    43.64 56.4 59.73                                                                     quartet triplet                                                                triplet singlet                                                                    49.6 27.3 24.6                                                                 1.6                 6  water                                                                               N,N'trimethyl Nhydroxy- ethyl ethylene diamine                                           ##STR24##      A B C D E F G                                                                    2.66 3.05 2.75 2.25 2.60 3.60 --                                                    singlet triplet triplet singlet                                                triplet triplet --                                                                  5.4 1.8 1.8 2.6 1.8 1.8                                                            43.8 58.82 52.25 41.76                                                         54.87 58.98 161.14                                                                   quartet triplet                                                                triplet quartet                                                                triplet triplet                                                                singlet                                                                            7.4 3.2 3.3                                                                    3.3 3.5 3.2                                                                    3.2                 7  water                                                                               TEDA                                                                                     ##STR25##      A B                                                                              3.05 --                                                                             singlet --                                                                          -- --                                                                              44.5 161.1                                                                           triplet singlet                                                                    19.3 2.53           __________________________________________________________________________

EXAMPLE 8

The same apparatus was used as in Examples 5-7. The flask was charged with 0.5 mole of TEDA, 0.5 mole of 2-methylimidizole, (a secondary amine of low basicity) and about 120 cc of water. Carbon dioxide was bubbled in till a gain of 22 gm (0.5 mole) was introduced. The reaction mixture was then analyzed by NMR. The product from this experiment, as shown in Table IV below was the triethylenediamine carbonate salt with free (unreacted) 2-methyl imidazole. No carbamate was formed which establishes the fact that carbamate formation requires secondary or primary amines of strong basicity.

                                      TABLE IV                                     __________________________________________________________________________     NMR Analysis for Product of Example 8                                           ##STR26##                                                                             H' NMR            C.sup.13 NMR                                         Chem.   Multi-                                                                               Integra-                                                                            Chem.  Multi-                                                                               Integra-                                       Shift, ppm                                                                             plicity                                                                              tion Shift, ppm                                                                            plicity                                                                              tion                                           __________________________________________________________________________     A 2.31(2.31).sup.a                                                                     singlet                                                                              1.93  12.81(13.7).sup.a                                                                    quartet                                                                              3.9                                            B 6.95(6.91).sup.a                                                                     singlet                                                                              1.18 121.19(121.1).sup.a                                                                   double                                                                               7.51                                           C --    --         145.73(144).sup.a                                                                     singlet                                                                              3.73                                           D 3.04(2.63).sup.b                                                                     singlet                                                                              8.4   44.97 triplet                                                                              23.78                                          E --    --         161.89 singlet                                                                              4.46                                           __________________________________________________________________________      .sup.a Chemical shifts for unreacted 2methyl/imidazole obtained from           Sadtler Standards.                                                             .sup.b Chemical shift for unprotonated TEDA.                             

EXAMPLE 9

Into a round bottomed flask fitted with a gas outlet tube and a thermometer, there was charged 50 grams of the product of Example 1. The gas outlet tube was connected by rubber tubing to a reservoir of a saturated solution of barium hydroxide. The flask was immersed in an oil bath and heated, while monitoring temperature and gas evolution. When the temperature of the solution inside the flask reached 33° C., bubbling of the gas into the barium hydroxide solution was observed. At 48° C. vigorous gas bubbling occurred with concomitant precipitation of barium carbonate, indicating that the liberated gas was carbon dioxide. When gas evolution ceased, the contents of the flask was cooled and weighed. A weight loss of 1.5 grams, or about 3% by weight of the total, was noted. The theoretical carbon dioxide content of the compound is 5% by weight. The pH of the decomposed product at 3% in distilled water and 25° C. was 9.3. The pH of a 3% solution of the undecomposed sample at 25° C. was 8.7.

From the foregoing example, it is apparent that the compounds of the present invention are thermally sensitive and decompose at about 50° C. to generate the active triethylenediamine (or other tertiary amine moiety of the starting compound) with liberation of CO₂, as evidenced by precipitation of barium carbonate and by the increase in the pH of the decomposed product. It is also noteworthy that the products of the present invention have a major advantage over other DAC amine catalysts in that they are of higher pH and thus less corrosive. In comparison, the pH of 3% DABCO WT® catalyst at 25° C. is about 3.2. DABCO WT catalyst is a commercial delayed action catalyst for polyurethane foams recommended for use in systems where long-range package stability is required. DABCO WT catalyst is comprised of a blend of hydroxypropylimidazole and a diformic acid salt of triethylenediamine.

EXAMPLE 10

The same procedure as that of Example 9 was used except that the tertiary amine carbonates salts of Examples 5-7 were decomposed. The decomposition temperature range and the pH of the solutions before and after decomposition are listed in Table V below.

                  TABLE V                                                          ______________________________________                                                               pH                                                       Carbonate Salt                                                                           Decomposition                                                                              After Decom-                                                                              pH Before                                     of Example                                                                               temp. range °C.                                                                     position   Decomposition                                 ______________________________________                                         6         55-80       9.9        8.7                                           8         40-85       9.4        8.3                                           ______________________________________                                    

It is evident from Table V above that the carbonate salts decompose irreversibly to regenerate the more basic free tertiary amines.

The compounds of the present invention are advantageously useful as delayed action catalysts in the preparation of polyurethane, particularly in molded microcellular applications as in shoe soles and automotive bumper fascia, highly resilient foams and other machine parts.

The following examples illustrate some of the advantages of the compounds of the present invention over standard commercial catalysts.

EXAMPLE 11

Catalysts of this invention were evaluated in a flexible foam formulation of the composition shown in Table VII, using "hand mix" technique.

                  TABLE VI                                                         ______________________________________                                         Component          pbw                                                         ______________________________________                                         Voranol ® 3010.sup.1                                                                          100                                                         Methylene chloride  20                                                         Silicone L6202.sup.2                                                                              1.5                                                         Water              3.6                                                         Catalyst           (as shown below)                                            Mondur ® T80.sup.3                                                                            46.1                                                        Hood temperature, 82-83° F.                                             ______________________________________                                         Catalyst         Conc., pbw                                                    ______________________________________                                         50% T-9.sup.4   0.6   0.8       0.6 0.8                                        DABCO ® TL.sup.5                                                                           0.4   0.4       --  --                                         Cat. of Ex. 1   --    --        0.6 0.6                                        ______________________________________                                         Reactivity                                                                     ______________________________________                                         Begin. of rise, secs                                                                             16     15       15   15                                      Rise time, secs  115    100      112  110                                      Hard gel, secs   145    130      130  117                                      Quality of foam  good   good     good good                                     ______________________________________                                          .sup.1 Voranol 3010 is a commercial polyether polyol of hydroxyl number        54.4-58.4; manufactured and sold by Dow Chemical Co.                           .sup.2 Silicone L6202 is a commercial silicone surfactant; distributed by      Union Carbide Corporation.                                                     .sup.3 Mondur TD80 is an 80/20 mixture of 2,4 and 2,6toluene diisocyanate      which has 48% NCO and an equivalent weight of 87; distributed by Mobay         Chemical Co.                                                                   .sup.4 T-9 is a trade name for stannous octoate sold by M & T Co.              .sup.5 DABCO TL catalyst is a proprietary mixture of DABCO 33LV defined i      Table VII below and DABCOT catalysts, both sold by Air Products and            Chemicals, Inc. DABCOT is N,N" trimethylhydroxy ethyl ethylene diamine.  

From the data in Table VI it is evident that the catalysts of the present invention are advantageous in that they provide for the same cream time (beginning of rise) but with much shorter hard gel time. This is of considerable importance to the manufacturer since he can speed up his conveyor line and increase output. It should be noted that the active concentration of amine in both the control and experimental catalysts is the same, namely, 0.21 parts per 100 of polyol.

EXAMPLE 12

The same procedure was used as that in Example 11 above except that the formulation was changed to that shown in Table VII below:

                  TABLE VII                                                        ______________________________________                                         FLEXIBLE FOAM FORMULATION                                                      Component       pbw                                                            ______________________________________                                         Voranol 3010    100                                                            Water           4.6                                                            Methylene chloride                                                                             7.0                                                            Silicone L6202  1.2                                                            Catalyst        as shown below                                                 Hylene TM.sup.6 62.5                                                           ______________________________________                                         Catalyst    Conc. pbw                                                          ______________________________________                                         T-9, 25% in DOP                                                                           1.2    1.2    1.2  1.2   1.2  1.2  1.2                              DABCO ®                                                                               0.1    0.15   0.2  --    --   --   --                               33-LV.sup.7                                                                    Cat. of Example 1                                                                         --     --     --   0.25  0.3  0.35 0.4                              ______________________________________                                         Reaction Profile                                                               ______________________________________                                         Beginning of                                                                               11    10      8    14    13  14   12                               rise, secs.                                                                    Hard gel, secs.                                                                           124    115    90   132   127  116  113                              Rise time, secs.                                                                          100    87     72   110   106  95   92                               Health bubbles                                                                            100    87     72   110   106  95   92                               ______________________________________                                          .sup.6 Hylene TM ia an 80/20 mixture of 2,4 and 2,6toluene diisocyanate        sold by duPont.                                                                .sup.7 DABCO ® 33-LV catalyst is a 33% by weight solution of TEDA in       dipropylene glycol; sold by Air Products and Chemicals, Inc.             

From the date in Table VII it is apparent that good flexible foams with extended cream and gel time are obtained using the catalysts of the present invention. This is particularly desirable when using new foam machinery such as the Maxfoam machines.

EXAMPLE 13

Catalysts of this invention were evaluated in high resilient foam (H.R.) formulation listed in Table VIII below using the "hand mix" technique. The reactants were mixed by a high speed mixer for ten seconds, then poured into an aluminum tray having a surface temperature of 100°-110° F. (38°-43° C.). After the material formed as a hard gel, it was placed in an oven at 150° F. (66° C.) and the tack-free time was determined. Table IX below shows the reaction profiles of H.R. foams made at various catalyst levels.

                  TABLE VIII                                                       ______________________________________                                         Component       pbw                                                            ______________________________________                                         8      NIAX ® 32-10                                                                            100.0                                                             Distilled water                                                                             3.3                                                        9      Freon 11B    6.0                                                        10     Silicone L5309                                                                              2.0                                                        11     T-12          0.005                                                            Amine Catalyst                                                                              as shown in Table IX                                       12     TDl/PAPl 80/20                                                                              42.0                                                       ______________________________________                                           8 NIAX 3210 is a polyol having an average hydroxyl number of 32.5; sold       by Union Carbide Corporation.                                                   9 Freon 11B is a trade name for fluorotrichloromethane; sold by du Pont.      10 L5309 is a brand of silicone surfactant; sold by Union Carbide              Corporation.                                                                   11 T12 is dibutyl tin dilaureate.                                              12 TDl/PAPl is a mixture of 2,4 and 2,6 toluene diisocyanate isomers with      a polymeric methylene bisdiphenyl isocyanate, the latter having an             equivalent weight of 133 and containing 31.5% of NCD; sold by Upjohn           Company.                                                                 

It is evident from Table IX above that the catalysts of the invention provide for longer gel time, hence good flow, and at the same time form tack-free foams at 150° F. (66° C.) much faster than the usual commercial catalysts, thereby affording shorter demold time and increased productivity. It is also to be noted that the active ingredient at the highest level used in the tests of Table IX is the same, namely, 0.5 parts of active triethylene diamine per 100 parts of polyol.

The foregoing examples are illustrative of the properties and characteristics of the compounds of the present invention. These compounds could be used in formulations with other well-known amine or amine salt co-catalysts as well as with other organometallic co-catalysts such as antimony catalysts, mercuric propionate and the like.

EXAMPLE 14

The tertiary amine carbonate salts were tested in a flexible foam formulation using the earlier described "hand mixing" techniques. The carbonate salts were compared to standard DABCO catalysts in presence of stannous octoate as the co-catalyst. The composition of the formulation and the reaction profiles obtained with the control and catalysts of this invention are shown on Table X below.

It is apparent from Table X that the carbonate salt provide for delaying cream by a factor of 2 while the gel is delayed by only 1.3 at a substantially lower level of amine catalyst. (See column 1, 3 and 5 of Table X.)

                                      TABLE X                                      __________________________________________________________________________                         Multranol 7100                                                                         100 parts                                                                              Room Temp. 62° F.                           FORMULATION:                                                                               Water    3.0 parts                                                                             Hood Temp. 58° F.                           Premix      Silicone L-540                                                                          1.0 parts                                                                             Reactant Temp. 23° C.                                   Catalyst                                                                               As Shown                                                               TDI 80/20                                                                               39.3 (107 index)                                  Catalyst        Concentration, parts per 359.8 parts of premix                 T-9 (Stannous                                                                            0.525                                                                              0.525                                                                               0.525                                                                              0.525                                                                               0.525                                                                              0.525                                                                               0.525                                                                               0.525                                                                               0.525                                                                               0.527                      Octoate)                                                                       DABCO ® 33LV                                                                         1.05                                                                               --   --  --   --  --   --   --   --   --                         NIAX A-1  0.7 --   --  --   --  --   --   --   --   --                                   (0.872)                                                              DABCO ® τ                                                                        --  1.2  --  --   --  --   --   --   --   --                         Cat. of Ex. 7                                                                            --  --   2.72                                                                               2.72 --  --   --   --   --   --                                            (0.6)                                                                              (0.6)                                                   Cat. of Ex. 4                                                                            --  --   --  --   2.96                                                                               2.96 --   --   --   --                                                     (0.64)                                                                             (0.64)                                         Cat. of Ex. 8                                                                            --  --   --  --   --  --   2.14 2.14 --   --                                                              (0.856)                                                                             (0.856)                              Cat. of Ex. 5                                                                            --  --   --  --   --  --   --   --   3.0  3.0                                                                       (1.05)                                                                              (1.05)                     Cream time (secs.)                                                                       8, 8                                                                               10   14  15   10  10   17   19   9    9                          Rise time (secs.)                                                                        72-95                                                                              134-195                                                                             155 155-195                                                                             85-155                                                                             100-160                                                                             175-200                                                                             140-185                                                                             150-215                                                                             132-210                    Hard Gel (secs.)                                                                         170 215  225 215  218 235  215  208  225  225                        __________________________________________________________________________ 

What is claimed is:
 1. The method for producing carbamate and carbonate salts of tertiary amines which comprises admixing a secondary amine with a tertiary amine in the presence of carbon dioxide under reaction conditions.
 2. The method as defined in claim 1 wherein said secondary amine is one corresponding to the formula ##STR27## wherein R₁ and R₂ are independently alkyl groups of 1 to 20 carbon atoms, in which the alkyl groups may contain one or more hydroxyl groups, or R₁ and R₂ can be a carbon atom-containing chain joined to the N to form a heterocyclic ring.
 3. The method as defined in claim 2 wherein R₁ and R₂ together constitute a carbon-containing chain joined to nitrogen and forming therewith a hetero ring from the group consisting of imidazole, morpholine and piperazine.
 4. The method as defined in claim 1 wherein said tertiary amine is one corresponding to the formula ##STR28## where R₃, R₄ and R₅ are independently alkyl of 1 to 3 carbon atoms, hydroxy alkyl of up to 3 carbon atoms, or R₃, R₄ and R₅ are organic radicals joined to the N to form a monocyclic or bicyclic hetero ring comprising tertiary nitrogen.
 5. The method as defined in claim 4 wherein R₃, R₄ and R₅ form a hetero ring from the group consisting of triethylenediamine, quinuclidine, N-alkyl piperazine and N-alkyl morpholine.
 6. The method as defined in claim 1, wherein said secondary and tertiary amines are reacted in equimolar amounts with excess of carbon dioxide.
 7. Compounds of the formula ##STR29## wherein R₁ and R₂ are independently alkyl groups of 1 to 20 carbons, which alkyl groups may contain one or more hydroxyl groups, or R₁ and R₂ are carbon containing radicals joined to form with N a hetero ring of 5 to 6 members; R₃, R₄ and R₅ are independently alkyl groups of 1 to 3 carbons, hydroxyalkyl groups of 1 to 3 carbons, or they can be organic radicals joined in a monocyclic or bicyclic hetero ring providing a cyclic tertiary amine moiety; or one of the groups R₁, R₂, R₃, R₄ or R₅ is an ethylene radical attached to another dialkyl amino alkyl group by an oxygen atom forming a ditertiary amine of the formula: ##STR30## where each R₆ independently is an alkyl group of 1 to 3 carbon atoms; n and m are independently 2 or
 3. 8. Compounds of the formula (I) of claim 7 wherein ##STR31## represents a heterocyclic secondary amine moiety from the group consisting of imidazole, morpholine, and piperazine and ##STR32## represents a heterocyclic tertiary amine moiety from the group consisting of triethylene diamine, quinuclidine, N-alkyl piperazine and N-alkyl morpholine.
 9. Compounds of the formula (I) of claim 7 wherein at least one R₃, R₄ and R₅ constitute the moiety of a ditertiary amine of the formula (II).
 10. Compounds of the formula (I) of claim 7 wherein R₃, R₄ and R₅ together are bis(N,N-dimethyl-amino)ethyl)ether.
 11. The compound of claim 7 which is the triethylene diamine salt of bis-hydroxyethyl carbamic acid.
 12. The compound of claim 7 which is the dimethylethanolamine salt of morpholino-carbamic acid.
 13. The compound of claim 7 which is the 2-methyltriethylene diamine salt of diethanolamino-carbamic acid.
 14. The compound of claim 7 which is the bis(dimethylaminoethyl)ether salt of carbamic and N-substituted carbamic acids.
 15. Formulations for the production of polyurethanes comprising as catalyst or co-catalyst therein a compound of the formula selected from the group consisting of ##STR33## wherein R₁, R₂, R₃, R₄ and R₅ are as defined in claim
 7. 16. Formulations for the production of polyurethanes comprising as catalyst or co-catalyst therein a compound as defined in claim
 8. 17. Formulations for the production of polyurethane comprising as catalyst or co-catalyst therein the compound of claim
 11. 18. In methods for the production of polyurethane by reaction of an organic isocyanate compound with a polyol, the improvement which comprises promoting said reaction with a catalyst composition comprising a tertiary amine salt of a carbamic acid compound, the nitrogen component of the carbamic acid comprising a substituent or substituents forming a secondary amine moiety.
 19. The improvement as defined in claim 18 wherein said catalyst composition comprises a compound as defined in claim
 8. 20. The improvement as defined in claim 18 wherein said catalyst composition comprises the compound recited in claim
 11. 